Table. 1. Table 1

Peaks other than Raman peak shift due to heat generation of laser power by root position (excluding the main peak). (a) Raman peak from positions #1 to #7. (b) Raman peak from position #8 to #12.

Position (µm)		Input Power (mW)	Raman Shift (cm-1)	Ratio of Intensity	Phase	References
#1	10	50	502.7	1	Si-IV	33
		45	499.1	0.91	Si-IV	49
		35	502.7	0.88	Si-IV	33
		25	508.5	0.94	Si-IV	49, 51–53
		25	498.1	0.70	Si-IV	23,54
		15	510.9	1.11	Si-IV	32,48
		15	505.2	0.78	Si-IV	49
		10	515.6	1.30	Si-IV	33,40,43–47
		10	498.8	0.59	Si-IV	43–47
		5	519.1	1.06	Si-I
		2.5	520.2	0.93	Si-I	9,33,41,50,56–59
		0.5	521.4	0.12	Si-I	24,32,49
#2	28	50	517.9	1	Si-IV	43
		10	513.2	0.33	Si-XII	3,42,49,61
		5	515.6	0.26	Si-IV	43–47
		0.5	522.6	0.04	Si-XII	56,60
#4	128	50	516.7	1	Si-IV	43
		50	507.0	0.62	Si-IV	33,43,44,45,47
		50	499.2	0.49	Si-IV	23,49
		45	502.7	0.39	Si-IV	33
		35	510.9	0.58	Si-IV	23,32,48
#5	171	35	493.3	0.44	Si-XIII	48,55
		25	498.0	0.47	Si-IV	23,54
		15	500.3	0.45	Si-IV	23,49,54
		10	508.8	0.74	Si-IV	23,49,51–53
#6	214	50	500.3	0.92	Si-IV	23,49,54
		45	494.5	1.0	Si-IV	43,44
		35	498.0	0.93	Si-IV	43,44
		25	503.8	0.86	Si-IV	33
		15	498.0	0.64	Si-IV	23,54
		10	494.5	0.37	Si-IV	43,44
#7	228	50	495.6	0.39	Si-XIII	48,55
		35	500.3	0.39	Si-IV	23,49,54
		25	495.6	0.29	Si-XIII	48,55
		10	505.0	0.32	Si-IV	49
(a)

Position (µm)		Input Power (mW)	Raman Shift (cm-1)	Ratio of Intensity	Phase	References
#8	250	35	492.1	0.74	Si-XII	48,55
		25	499.2	0.57	Si-IV	23,49
		15	515.6	0.99	Si-IV	43–47
		15	508.5	0.70	Si-IV	23,49,51–53
		15	496.8	0.47	Si-XIII	48,55
		5	498.0	0.18	Si-IV	23,54
		2.5	515.6	0.38	Si-IV	23,32
#9	271	25	515.6	1	Si-IV	23,32
		25	498.0	0.38	Si-IV	23,54
		0.5	522.6	0.07	Si-XII	56,60
#10	285	25	507.4	0.57	Si-IV	33,43–45,47
		25	493.3	0.48	Si-XIII	48,55
		15	510.9	0.52	Si-IV	32,48
		15	499.2	0.45	Si-IV	23,49
		10	512.0	0.51	Si-XII	3,42,49,61
		10	500.3	0.42	Si-IV	23,49,54
#11	300	50	505.0	1	Si-IV	49
		50	498.0	0.98	Si-IV	23,54
		25	512.0	1.01	Si-XII	3,43,49,61
		25	494.5	0.73	Si-IV	43,44
		15	514.4	1.01	Si-IV	23,32
		15	508.5	0.85	Si-IV	23,49,51–53
		15	495.6	0.58	Si-XIII	48,55
#12	335	50	496.8	1	Si-XIII	48,55
		45	499.2	1.40	Si-IV	23,49,54
		35	502.8	0.77	Si-IV	33
		25	495.6	1.34	Si-XIII	48,55
		15	509.7	0.70	Si-IV	23,32,48
		15	494.5	0.93	Si-XIII	48,55
		10	510.9	0.97	Si-IV	23,32,48
		10	500.3	0.64	Si-IV	23,49,54
		5	515.6	0.64	Si-IV	32,43,45–47,52
		5	509.7	0.61	Si-IV	32
		2.5	517.9	0.88	Si-IV	43
		0.5	521.4	0.16	Si-I	32,41
(b)

New Phys.: Sae Mulli 2021;71:827~837 https://doi.org/10.3938/NPSM.71.827

© NPSM