Crystallization and Dielectric Properties of Amorphous KNbGeO5

C. H. SONG1, H. W. CHOI1, D. G. KANG1, J. E. KIM1, J. K. LEE1, Y. S. YANG1*, S. J. KIM2

1Department of Physics, RCDAMP, Pusan National University, Busan 609-735
2School of Nano Science and Technology, Busan 609-735

Correspondence to:ysyang@pusan.ac.kr

Abstract

The crystallization mechanism and the dielectric property of amorphous KNbGeO5 were studied. Differential scanning calorimetry was used to investigate the crystallization mechanism. The dielectric property was measured by using an impedance/gain-phase analyzer in the frequency range 100 Hz ~ 15 MHz with the heating rate of 2 oC/min. Crystallization was found to occur through a 3-dimensional growth with an activation energy of 8.1 eV and a crystallization parameter of 4. There was an abrupt increase in both the real and the imaginary parts of the dielectric constant for glass in the crystal transition region due to the active motions of atoms and molecules.

Keywords: Crystallization, Nanocrystal, Dielectric property

KNbGeO$_5$ 유리를 제조하여 결정화 과정 및 유전특성에 관하여 연구하였다. 결정화 과정은 열분석 장치를 이용하여 비등온 방식으로 실험하였다. 전기적 특성은 Impedance~/Gain-Phase 분석기를 이용해 2 $^\circ$C/min의 승온율로 상온에서 800 $^\circ$C의 온도구간에서 그리고 주파수는 100 Hz $\sim$ 15 MHz 범위에서 측정하였다. KNbGeO$_5$ 유리의 결정화에 필요한 활성화 에너지는 8.1 eV이였으며, 결정화 기구를 나타내는 맺음변수는 4로써 초기 비정질에서 핵을 생성하면서 3차원 성장을 함을 확인하였다. 유전특성은 유리전이 구간에서부터 결정화 구간에 걸쳐 원자 및 분자들의 활발한 움직임으로 실수부와 허수부 모두 급격한 증가를 보였다.

Keywords: <P>결정화, 나노결정, 유리, 유전특성</P>